Title: Optimization of the sintering process of raw material wastes
Authors: Vieira, M. T. 
Catarino, L. 
Oliveira, M. 
Sousa, J. 
Torralba, J. M. 
Cambronero, L. E. G. 
González-Mesones, F. L. 
Victoria, A. 
Keywords: Powder technology; Ceramics
Issue Date: 1999
Citation: Journal of Materials Processing Technology. 92-93:(1999) 97-101
Abstract: The analysis of the mineralogical composition of most rock wastes shows the presence of a high percentage of minerals with SiO2 and Al2O3, which could be used as raw materials for ceramic products. The main objective of this work is to recover wastes from one primary rock industry, utilised in the production of tiles and flooring, for the manufacturing of ceramics, using powder technology: pressing and sintering. The sinterability of the powders, with and without previous heat treatment, was studied in order to obtain a product with the best performance. Powders from different quarries after being uniaxial pressed at 40 MPa, or isostatic pressed at 170 MPa and sintered within the range 1150-1170°C present properties as follows: (a) hardness: 5.5-7.5 GPa; (b) transverse rupture strength: 55-94 MPa; (c) abrasion and erosion wear better than that of bulk to be drawn materials, and (d) water absorption of less than 0.5%. The results allow the conclusion that these wastes can be recovered and used successfully in the manufacture of ceramics with better performance than traditional tiles and flooring.
URI: http://hdl.handle.net/10316/4313
Rights: openAccess
Appears in Collections:FCTUC Eng.Mecânica - Artigos em Revistas Internacionais

Files in This Item:
File Description SizeFormat
file2278c601b4ee45a8b1b4aff068e3a349.pdf402.85 kBAdobe PDFView/Open
Show full item record

Page view(s) 50

243
checked on Oct 16, 2019

Download(s) 5

1,928
checked on Oct 16, 2019

Google ScholarTM

Check


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.