Title: Control of eta carbide formation in tungsten carbide powders sputter-coated with (Fe/Ni/Cr)
Authors: Fernandes, C. M. 
Senos, A. M. R. 
Vieira, M. T. 
Keywords: Tungsten carbide; Coated powders; Fe/Ni/Cr; [eta]-phase
Issue Date: 2007
Citation: International Journal of Refractory Metals and Hard Materials. 25:4 (2007) 310-317
Abstract: Composite powders of tungsten carbide with variable coating contents of Fe/Ni/Cr based alloys (1-15 wt.%) were prepared by sputtering. The coated powders have revealed a good performance to shape-forming and sintering. However, the presence of nanocrystalline coatings could enhance the formation of a brittle phase during sintering, named [eta]-phase, (M, W)6C. To investigate this effect, the powders were heat-treated at variable temperatures, up to 1400 °C. For comparison, conventionally prepared powders were studied, too, and the content of [eta]-phase was found to be higher for the sputter-coated ones. This result is attributed to the content of binder elements with affinity to carbon, like chromium, enhanced by the difference on binder characteristics, such as nanocrystallinity and morphology. It was concluded that an effective control of the reaction can be achieved by increasing in the binder composition the ratio between the elements without affinity and those with affinity to carbon and/or enlarging the carbon content.
URI: http://hdl.handle.net/10316/4201
Rights: openAccess
Appears in Collections:FCTUC Eng.Mecânica - Artigos em Revistas Internacionais

Files in This Item:
File Description SizeFormat
file88a497e87f364cae976c3b4899eb483f.pdf537.35 kBAdobe PDFView/Open
Show full item record

Page view(s)

105
checked on Oct 15, 2019

Download(s)

109
checked on Oct 15, 2019

Google ScholarTM

Check


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.